Industrial polyurethane powder coating

Industrial polyurethane powder coating

Product Description: This series of products is saturated hydroxyl poly resin and special crosslinking agent, weathering organic and inorganic pigments based on the preparation of a thermosetting polyurethane powder coating. With excellent leveling, excellent light resistance and excellent weather resistance and better pencil hardness. Powder performance: Specific gravity 1.3-1.7 g / cm (depending on color and formula) Particle size measurement Average particle size D50: 20-25 microns Packaging 20KG carton packaging, lined with plastic bags Storage period of 8 months (25 ℃ constant temperature) Application tools Corona electrostatic spraying / friction Sassafras live spray Coating thickness 30-40 microns (depending on the spray material) Coated area of ​​14-16 square meters per kilogram (theoretical area) Curing conditions 180 ° C / 15 minutes or 200 ° C / 10 minutes (material surface temperature) Coating appearance Gloss (60 ° angle) 80-90% high light; 40-70% half light; 15-35% matte; ≤ 15% matte. Smooth or wrinkle effects and special effects Mechanical behavior Experimental tinplate degreasing phosphating model, film thickness 60-80 microns, the national standard experimental conditions to complete. Pencil hardness GB / T6739-86 2H-4H Adhesion GB / T9286-88 Level 0 Bending experiment GB / T11185-88 0 Cup test (Eriksson value) GB / T9753-88 8 mm Impact Experiment GB / T1732-93 Positive / Reverse 1 KG / 50cm Corrosion resistance All experimental samples are degreasing phosphating method, the film thickness of 90-100 microns in the national standard experimental conditions to complete. Salt spray test ASTMB117 / GB1771-91 2000 hours after no effect, and cross-section corrosion less than 2 mm. Hot and humid experiment BS.3900PART F2 1793 3000 hours; GB1740 / 799 (89) 1000 hours after no effect, slightly lost light. Applications Indoor and outdoor furniture / household appliances / automotive interior parts / machinery / toys IMPORTANT: Our oral and written presentations regarding the use of the product are derived from our experience and are based on current technical standards. Purpose To provide assistance to customers and users, they do not assume any obligations or purchase agreements Assume any responsibility for the user to verify the suitability of the product before using the product.

Classification:

Nano Fluorocarbon Coating

Keywords:

High temperature PVDF fluorocarbon coatings

Product description

Product Description: This series of products is saturated hydroxyl poly resin and special crosslinking agent, weathering organic and inorganic pigments based on the preparation of a thermosetting polyurethane powder coating. With excellent leveling, excellent light resistance and excellent weather resistance and better pencil hardness.

Powder performance:

Specific gravity 1.3-1.7 g / cm (depending on color and formula)

Particle size measurement Average particle size D50: 20-25 microns

Packaging 20KG carton packaging, lined with plastic bags

Storage period of 8 months (25 ℃ constant temperature)

Application tools Corona electrostatic spraying / friction Sassafras live spray

Coating thickness 30-40 microns (depending on the spray material)

Coated area of ​​14-16 square meters per kilogram (theoretical area)

Curing conditions 180 ° C / 15 minutes or 200 ° C / 10 minutes (material surface temperature)

Coating appearance

Gloss (60 ° angle)

80-90% high light; 40-70% half light; 15-35% matte; ≤ 15% matte.

Smooth or wrinkle effects and special effects

Mechanical behavior

Experimental tinplate degreasing phosphating model, film thickness 60-80 microns, the national standard experimental conditions to complete.

Pencil hardness GB / T6739-86 2H-4H

Adhesion GB / T9286-88 Level 0

Bending experiment GB / T11185-88 0

Cup test (Eriksson value) GB / T9753-88 8 mm

Impact Experiment GB / T1732-93 Positive / Reverse 1 KG / 50cm

Corrosion resistance

All experimental samples are degreasing phosphating method, the film thickness of 90-100 microns in the national standard experimental conditions to complete.

Salt spray test ASTMB117 / GB1771-91 2000 hours after no effect, and cross-section corrosion less than 2 mm.

Hot and humid experiment BS.3900PART F2 1793 3000 hours; GB1740 / 799 (89) 1000 hours after no effect, slightly lost light.

Applications Indoor and outdoor furniture / household appliances / automotive interior parts / machinery / toys

IMPORTANT: Our oral and written presentations regarding the use of the product are derived from our experience and are based on current technical standards. Purpose To provide assistance to customers and users, they do not assume any obligations or purchase agreements Assume any responsibility for the user to verify the suitability of the product before using the product.