Epoxy polyester type coating

Epoxy polyester type coating

Product Description: This series of products is epoxy polyester resin mixture, curing agent and pigment based on the preparation of a thermosetting powder coating. Its lightfastness and heat resistance are better than epoxy powder coatings. The Powder performance: the proportion of 1.3-1.7 g / cubic centimeter (due to different colors and recipes) Particle size determination: Average particle size D50: 20-25 microns Packaging 20KG carton packaging, lined with plastic bags Storage period of 8 months (25 ℃ constant temperature) Application tools Corona electrostatic spraying / friction Sassafras live spray Coating thickness 40-50 microns (depending on the spray material) Coated area of ​​14-16 square meters per kilogram (theoretical area) Curing conditions 160 ° C / 25 minutes and 180 ° C / 15 minutes or 200 ° C / 10 minutes (material surface temperature) Appearance of the coating gloss (60 degrees angle) 80-90% high light; 40-70% half light; 15-30% matte; ≤ 15% matte. Smooth or wrinkle effect and special effects machine Mechanical performance test tinplate degreasing phosphating model, film thickness 40-60 microns, the national standard experimental conditions to complete. Pencil hardness GB / T6739-86 2H-4H Adhesion GB / T9286-88 Level 0 Bending experiment GB / T11185-88 0 Cup test (Eriksson value) GB / T9753-88 6-8 mm Impact Experiment GB / T1732-93 Positive / Reverse 1 KG / 50cm Corrosion resistance All test panels are degreased with phosphating method, the film thickness of 90-100 microns in the national standard experimental conditions to complete. Salt spray test ASTMB117 / GB1771-91 1000 hours after no effect, and cross-section corrosion less than 2 mm. Hot and humid experiment BS.3900PART F2 1793 3000 hours; GB1740 / 799 (89) 1000 hours after no effect, slightly lost light. Applications Office furniture / household appliances / automotive interior parts / machinery / toys Note: This series of products can not be used for outdoor use, or will make the film discoloration, fading, powder and other issues. IMPORTANT: Our oral and written presentations regarding the use of the product are derived from our experience and are based on current technical standards. Purpose To provide assistance to customers and users, they do not assume any obligations or purchase agreements Assume any responsibility for the user to verify the suitability of the product before using the product.

Classification:

Nano Fluorocarbon Coating

Keywords:

High temperature PVDF fluorocarbon coatings

Product description

Product Description: This series of products is epoxy polyester resin mixture, curing agent and pigment based on the preparation of a thermosetting powder coating. Its lightfastness and heat resistance are better than epoxy powder coatings.

The Powder performance: the proportion of 1.3-1.7 g / cubic centimeter (due to different colors and recipes)

Particle size determination:

Average particle size D50: 20-25 microns

Packaging 20KG carton packaging, lined with plastic bags

Storage period of 8 months (25 ℃ constant temperature)

Application tools Corona electrostatic spraying / friction Sassafras live spray

Coating thickness 40-50 microns (depending on the spray material)

Coated area of ​​14-16 square meters per kilogram (theoretical area)

Curing conditions 160 ° C / 25 minutes and 180 ° C / 15 minutes or 200 ° C / 10 minutes (material surface temperature)

Appearance of the coating gloss (60 degrees angle)

80-90% high light; 40-70% half light; 15-30% matte; ≤ 15% matte.

Smooth or wrinkle effect and special effects machine

Mechanical performance test tinplate degreasing phosphating model, film thickness 40-60 microns, the national standard experimental conditions to complete.

Pencil hardness GB / T6739-86 2H-4H

Adhesion GB / T9286-88 Level 0

Bending experiment GB / T11185-88 0

Cup test (Eriksson value) GB / T9753-88 6-8 mm

Impact Experiment GB / T1732-93 Positive / Reverse 1 KG / 50cm

Corrosion resistance All test panels are degreased with phosphating method, the film thickness of 90-100 microns in the national standard experimental conditions to complete.

Salt spray test ASTMB117 / GB1771-91 1000 hours after no effect, and cross-section corrosion less than 2 mm.

Hot and humid experiment BS.3900PART F2 1793 3000 hours; GB1740 / 799 (89) 1000 hours after no effect, slightly lost light.

Applications Office furniture / household appliances / automotive interior parts / machinery / toys

Note: This series of products can not be used for outdoor use, or will make the film discoloration, fading, powder and other issues.

IMPORTANT: Our oral and written presentations regarding the use of the product are derived from our experience and are based on current technical standards. Purpose To provide assistance to customers and users, they do not assume any obligations or purchase agreements Assume any responsibility for the user to verify the suitability of the product before using the product.